Pulp beating (refining) freeness tester TP-C10 is used to measure the rate of dilution of pulp suspended water materials and to determine de-watering time. It is adopted with spring pre-tightening mechanism keeps the rubber sealing ring of the sealing hammer body in contact with the bottom of the water filtering tube. This increases the sealing performance of the sealing hammer body.
| Measurement range | 0 to 100° SR |
|---|---|
| Slider weight | |
| Slider size | |
| Testing accuracy | |
| Dimension of working plate | |
| Speed of slider | |
| Slider stroke | |
| Specimen size | |
| Division value | |
| Number of specimen holders | |
| Metal Cylinder inner area | |
| Metal Cylinder height | |
| Metal roller width | |
| Metal roller weight | |
| Absorbency paper | |
| Absorbency speed | |
| Sealed testing speed | 100 ± 10 mm/s |
| Volume of distilled water | 1000 ± 5 ml |
| Sample diameter | |
| Sample error | |
| Sample Thickness | |
| Draining time | 149 ± 1 s |
| Residual water volume | 7.85 to 8 ml |
| Hydraulic pressure | >0.3 MPa |
| Dimension | 450×250×1100 mm |
| Net Weight | 40 kg |
Pulp beating freeness tester has applications in pulp & paper industry, packaging industry.
| Measurement range | 0.01 to 10 N |
| Slider weight | 200 g |
| Slider size | 63×63 mm |
| Testing accuracy | ± 2 % |
| Capacity | A: 20 to 500 J/m2 B: 500 to 1000 J/m2 |
| Impact angle | 90° |
| Unit | Lb-ft/in2 J/m2 |
| Error | A: ± 1 J/m2 B: ± 2 J/m2 |
| Metal Cylinder inner area | (100 ± 0.2) cm2 |
| Metal Cylinder height | 50 mm |
| Metal roller width | (200 ± 0..5) mm |
| Metal roller weight | (10 ± 0.5) kg |
| Measuring range | 0 to 20 mm |
| Accuracy | 0.01 mm |
| Gauge | Analogue gauge display |
| Contact pressure (to create false weight) | 20 ± 0.5 kPa |
| Sample width | 15 mm |
| Sample maximum length | 300 mm |
| Parallelism | ≤ 0.1 mm |
| Dimension | 240×520×70 mm |
| Testing speed | 200° ± 20° / min |
| Test range | 1 to 10000 mN |
| Indicating Error | ± 1 % |
| Testing length | 5, 10, 15, 20, 25, 50 mm |
| Sample (size) length | 90 to 200 mm |
| Sample width | 15 mm, 25 mm, 50mm |
| Measuring range | 0 to 30, 0 to 100 N,0 to 300 N |
| Accuracy | ± 1 % |
| Measurement range | 5 to 500 N, 50 to 3000 N |
| Resolution | 1 N |
| Accuracy | ± 1 % |
| Variability | ≤ 1 % |
| Sample size (L*B) | 230×50 mm (can join short samples together) |
| Rub pressure | 20 ± 0.2 N |
| Friction speed | 43 times / min |
| Friction area (L*B) | 155×50 mm |
| Sample (size) length | Diameter ≥30 mm, Thickness ≤ 40 mm |
| Measurement mode | Diffuse reflection factor Rx, Ry, Rz, stimulus value Y10, X10, Z10, chromaticity coordinates x10, y10, z10; lightness L *, chroma a * b *, chroma C * ab, hue angle h * ab, dominant wavelength λd, excitement purity Pe, color difference ΔE * ab, lightness difference ΔL *, chroma difference ΔC * ab, hue difference ΔH * ab, Hunter system L , A, b |
| Stability | ≤ 0.1 within 30 min |
| Accuracy | Chromaticity co-ordinate 0.0001 |
| Measuring range | A (1 to 6) J indicating error ± 0.05 J<br/> B (1 to 12) J indicating error ± 0.05 J<br/> C (1 to 24) J indicating error ± 0.05 J<br/> D (1 to 48) J indicating error ± 0.05 J<br/> The indicating errors w.r.t measurement range of 20 to 80 % |
| Frictional resistance | <0.25 J |
| Pyramid dimension | Three sides: 60×60×60 mm, height 25 ± 0.7 mm, Arris edge fillet radius 1.5 ± 0.1 mm |
| Dimension | 800×470×840 mm |
| Sample (size) length | 0 to 200 mm adjustable |
| Sample width | 15 mm |
| Measuring range | 0 to 30 N (tissue paper), 0 to 100 N,0 to 300 N, 0 to 500 N, 0 to 1000 N |
| Accuracy | ± 1 % |
| Measuring scope | ( 1 to 9999) s, divided in to (1 to 15) s, (15 to 300) s, (300 to 9999) s, the automatic (no. more than 200 s) |
| Accuracy | ±0.1 s within 300 s |
| Vacuum system volume (ml) | Bigger volume: 380 ± 1<br/> Smaller volume: 38 ± 1 |
| Contact pressure | 100 ± 2 kPa |
| Measurement range | 0 to 1600 kPa |
| Accuracy | ± 0.5 % F.S. |
| Compression speed | 95 ± 5 ml/min |
| Clamp pressure | ≥ 430 kPa |
| Measuring range | 0 to 1000 mN |
| Resolution | 0.1 mN |
| Indication error | ± 1 % |
| Tearing arm | 104 ± 1 mm |
| Sample (size) length | 38×70 mm |
| Measuring range | (1-500) mN.m (divided into 7 small ranges) |
| Indication error | 0.02 |
| Test speed | (200° ± 20°)/ min |
| Sample (size) length | Diameter ≥30 mm, Thickness ≤ 40 mm |
| System | D/0 lighting geometrical viewing conditions, diffuser diameter (d) 150mm, testing hole diameter 30mm |
| Light source | D65 as illuminating source |
| Zero drift | ≤ 0.1 % |
| Sample (size) length | Diameter ≥30 mm, Thickness ≤ 40 mm |
| Measurement mode | Diffuse reflection factor Rx, Ry, Rz, stimulus value Y10, X10, Z10, chromaticity coordinates x10, y10, z10; lightness L *, chroma a * b *, chroma C * ab, hue angle h * ab, dominant wavelength λd, excitement purity Pe, color difference ΔE * ab, lightness difference ΔL *, chroma difference ΔC * ab, hue difference ΔH * ab, Hunter system L , A, b |
| Stability | ≤ 0.1 within 30 min |
| Accuracy | Chromaticity co-ordinate 0.0001 |
| Measuring range | 0.001 to 9999 |
| Stability | A (absorbency of light) <0.003 within 3 mins |
| Linearity error | <3.0 % |
| Repeatability error | A (absorbency of light) <0.005 |
| Measuring range | 0.001 to 9999 |
| Stability | A (absorbency of light) <0.003 within 3 mins |
| Linearity error | <3.0 % |
| Repeatability error | A (absorbency of light) <0.005 |
| Salinity Measurement range | 0.00 to 19.99 ms/cm |
| Measuring accuracy | EC ± 2% full scale |
| Temperature Measurement range | -5 to 50°C |
| Temperature accuracy | ± 0.5°C |
| Mixed capacity | 0.5 to 1 kg, 2 to 3 kg, 5 to 7 kg |
| Temperature range | RT to 300°C |
| Temperature control system | PID control |
| Display | LED display |
| Test arm weight | 2.5 N |
| Additional Loads | 2.5 ± 0.1 N, 5 ± 0.1 N, 10 ± 0.1 N, |
| Idler | 150 mm |
| Abrasion stroke | 40 ± 0.2 M |
| Temperature control range | Room temperature to -70 ℃ (room temperature ≤ 25 ℃） |
| Temperature accuracy | ± 0.3 ℃ |
| Impact speed | 0℃ to -30℃ around 2.5 ℃/min </br> -30℃ to -40℃ around 2.5 ℃/min </br> -40℃ to -70℃ around 2.0 ℃/min</br> |
| Max dimension L × W × H | 910 × 510 × 860 mm |
| Preliminary test force | 98 N |
| Total test force | 588, 980, 1471 N |
| Total test force dwell time | 1 to 30 S |
| Hardness indication | Digital display |
| Preliminary test force | 98 N |
| Total test force | 588, 980, 1471 N |
| Total test force dwell time | 0 to 30 S |
| Hardness indication | Analogue display |
| Preliminary test force | 98 N |
| Total test force | 588, 980, 1471 N |
| Brinell hardness test | 306, 613, 1839 N |
| Vickers hardness test | 294, 588, 980 N |
| The maximum temperature | 300°C |
| Temperature fluctuation | Within ± 0.5°C |
| Temperature uniformity | Within ± 1°C |
| Rotate speed of the turntable | 11 r/min to 12r/min, turntable dimension diameter: 285 mm |
| Resolution | 0.1 % O2 |
| Measuring range | 0 to 100 % O2 |
| Precision | ± 0.4 % O2 |
| Response time | < 10 S |
| Vacuum degree | 0 to 90 KPa |
| Accuracy | 1 % FS |
| Resolution | 0.1 KPa |
| Vacuum chamber effective size | 270 × 210 mm |