Ink rubber tester TP-F10 with benchtop design is used to measure printing ink layers decolorization, rub resistance on low or high printable surface. This tester effectively analyzes the problems of ink decolorization, poor abrasion resistance, photosensitive coating. It helps in identifying the quality of ink and printing method to be used in industry.
| Sample size (L*B) | 230×50 mm (can join short samples together) |
| Rub pressure | 20 ± 0.2 N |
| Friction speed | 43 times / min |
| Friction area (L*B) | 155×50 mm |
| No. of friction | 0 to 999, auto shutdown |
| Dimension | 275×302×297 mm |
| Weight | 25 kg |
| Power supply | AC220 V ± 10 % , 50 Hz |
| Sample (size) length | 0 to 200 mm adjustable |
| Sample width | 15 mm |
| Measuring range | 0 to 30 N (tissue paper), 0 to 100 N,0 to 300 N, 0 to 500 N, 0 to 1000 N |
| Measuring range | A (1 to 6) J indicating error ± 0.05 J<br/> B (1 to 12) J indicating error ± 0.05 J<br/> C (1 to 24) J indicating error ± 0.05 J<br/> D (1 to 48) J indicating error ± 0.05 J<br/> The indicating errors w.r.t measurement range of 20 to 80 % |
| Sample (size) length | 180 mm (180, 150, 100, 90, 50 mm adjustable) |
| Sample width | 15 mm |
| Measuring range | 0 to 30, 0 to 100 N,0 to 300 N, 0 to 500 N, 0 to 1000 N |
| Sample (size) length | 38×70 mm |
| Measuring range | (1-500) mN.m (divided into 7 small ranges) |
| Measuring scope | ( 1 to 9999) s, divided in to (1 to 15) s, (15 to 300) s, (300 to 9999) s, the automatic (no. more than 200 s) |
| Measurement range | 0.01 to 10 N |
| Slider weight | 200 g |
| Slider size | 63×63 mm |
| Sample (size) length | 90 to 200 mm |
| Sample width | 15 mm, 25 mm, 50mm |
| Measuring range | 0 to 30, 0 to 100 N,0 to 300 N |
| Operating temperature | Ambient temperature to 300°C |
| Heating rate | 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min) |
| Maximum temp. error with heating speed | ± 5°C under 50°C/ h, ± 1°C under 120°C/ h |
| Seal temperature | Room temperature -250°C |
| Control accuracy | ± 0.2°C |
| Dwell time | 0.1 S to 999.9 S |
| Measuring range | 0.01 to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm/ 10 min (MVR), 0.001 to 9.999 g/cm (melt density) |
| Measuring rate | 0.001 S |
| Temperature range | 50 to 400°C |
| The maximum temperature | 300°C |
| Temperature fluctuation | Within ± 0.5°C |
| Temperature uniformity | Within ± 1°C |
| Standard roller | 2000 ± 50 g |
| Testing stations | 6 |
| Dimension (L*W*H) tester | 650×210×550 mm (6 stations) |
| Measuring range | 0.01to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm3/ 10 min (MVR), 0.001 to 9.999 g/ cm3 (melt density) |
| Measuring rate | 0.001 S |
| Temperature range | 50 to 400°C |
| Standard roller | 2000 ± 50 g |
| Testing stations | 3 |
| Dimension (L*W*H) tester | 320×210×550 mm (3 stations) |
| Inclined adjustable angle | 0 to 40° |
| Panel width | 120 mm |
| Test area width | 80 mm |
| Impact Speed & Energy (charpy) | 2.9 m/s for 1J, 2J, 4J, 5J & 3.8 m/s for 7.5J, 15J, 25J |
| Impact energy (Izod) | 3.5 m/s for 1J, 2J, 4J, 5J, 7.5J, 15J, 25J |
| Resolution of impact energy | 0.001 J |
| Test arm weight | 2.5 N |
| Additional Loads | 2.5 ± 0.1 N, 5 ± 0.1 N, 10 ± 0.1 N, |
| Idler | 150 mm |
| Temperature range | RT 50° to 300° |
| Temperature accuracy | ± 1° |
| Measuring range | 0.01 to 25 mm |
| Temperature control range | Room temperature to -70 ℃ (room temperature ≤ 25 ℃） |
| Temperature accuracy | ± 0.3 ℃ |
| Impact speed | 0℃ to -30℃ around 2.5 ℃/min </br> -30℃ to -40℃ around 2.5 ℃/min </br> -40℃ to -70℃ around 2.0 ℃/min</br> |
| Mixed capacity | 0.5 to 1 kg, 2 to 3 kg, 5 to 7 kg |
| Temperature range | RT to 300°C |
| Temperature control system | PID control |
| Temperature range | -60°C to 0°C |
| Temperature accuracy | ± 0.5°C |
| Preliminary test force | 98 N |
| Total test force | 588, 980, 1471 N |
| Brinell hardness test | 306, 613, 1839 N |
| Frequency (continually adjustable) | 10 Hz to1280 Hz + 0.01 % |
| Amplitude acceleration ( at 30m/s2 pk ) | 40 Hz to 320 Hz + 0.3 dB + 1 digit |
| Amplitude velocity ( at 25mm / sec pk ) | 40 Hz to 320 Hz + 0.5dB +1 digit |
| Test force | 612.5 N, 980 N, 1225 N |
| Brinell hardness test | 1837.5 N, 2450 N, 4900 N/7350 N, 9800 N, 14700 N/29400 N |
| Hardness measuring area | 8 to 650 HBW (hard metals steel ball) |
| Measuring range | 0.001 to 9999 |
| Stability | A (absorbency of light) <0.003 within 3 mins |
| Linearity error | <3.0 % |
| Measurement range | 0 to 80 % |
| Resolution | 0.1 |
| Accuracy | ± 2 % n (non-saturation condition) |
| Salinity Measurement range | 0.00 to 19.99 ms/cm |
| Measuring accuracy | EC ± 2% full scale |
| Temperature Measurement range | -5 to 50°C |
| Maximum load | 100 kg ( kg and N can be switched automatically) |
| Resolution | 0.01 g |
| Accuracy | ± 0.5 % |
| Measurement range | 0 to 90 % |
| Resolution | 0.1 or 0.01 |
| Accuracy | ± 5 % n (non-saturation condition) |
| Maximum load | 100 kg ( kg and N can be switched automatically) |
| Resolution | 0.01 g |
| Accuracy | ± 0.5 % |
| Measuring range | 0.001 to 9999 |
| Stability | A (absorbency of light) <0.003 within 3 mins |
| Linearity error | <3.0 % |
| Measurement range | 0 to 60 % |
| Resolution | 0.1 |
| Accuracy | ± 5 % n (non-saturation condition) |