Heat sealer THS-A10 works on heat press seal method, before start of the test, user needs to preset the heat seal temperature, pressure and dwell time values so as to finish the entire sealing process automatically just after pressing the start button. Equipped with digital P.I.D. temperature control technology ensures the preset temperature to be reached rapidly without any fluctuation. The specimen is placed in between the upper & lower jaws with independent temperature control of upper & lower jaws.
| Seal temperature | Room temperature -250°C |
|---|---|
| Control accuracy | ± 0.2°C |
| Dwell time | 0.1 S to 999.9 S |
| Dwell pressure | 0.05 to 0.7 MPa |
| Heating mode | Single and double heating surface |
| Dimension (L*B*H) | 400×280×380 mm |
| Net weight | 30 kg |
| Power supply | AC 220V/ 50Hz |
Heat sealer is used in plastic film material packaging, soft packaging laminated film & others to heat seal material using temperature, heat, pressure.
| Measuring range | 0.01to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm3/ 10 min (MVR), 0.001 to 9.999 g/ cm3 (melt density) |
| Measuring rate | 0.001 S |
| Temperature range | 50 to 400°C |
| Temperature precision | ± 0.5°C |
| Standard roller | 2000 ± 50 g |
| Testing stations | 6 |
| Dimension (L*W*H) tester | 650×210×550 mm (6 stations) |
| Weight for stations | 15 kg (6 stations) |
| The maximum temperature | 300°C |
| Temperature fluctuation | Within ± 0.5°C |
| Temperature uniformity | Within ± 1°C |
| Rotate speed of the turntable | 11 r/min to 12r/min, turntable dimension diameter: 285 mm |
| Impact Speed & Energy (charpy) | 2.9 m/s for 1J, 2J, 4J, 5J & 3.8 m/s for 7.5J, 15J, 25J |
| Impact energy (Izod) | 3.5 m/s for 1J, 2J, 4J, 5J, 7.5J, 15J, 25J |
| Resolution of impact energy | 0.001 J |
| Pendulum up angle | 160° |
| Inclined adjustable angle | 0 to 40° |
| Panel width | 120 mm |
| Test area width | 80 mm |
| Standard steel balls | 1/32 to 1 inch |
| Temperature range | 10 to 35°C |
| Maximum falling height | 2000 mm |
| Resolution of displacement | 1 mm |
| Height error | < ± 2 mm |
| Standard roller | 2000 ± 50 g |
| Testing stations | 3 |
| Dimension (L*W*H) tester | 320×210×550 mm (3 stations) |
| Weight for stations | 10 kg (3 stations) |
| Resolution | 0.1 % O2 |
| Measuring range | 0 to 100 % O2 |
| Precision | ± 0.4 % O2 |
| Response time | < 10 S |
| Operating temperature | Ambient temperature to 300°C |
| Heating rate | 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min) |
| Maximum temp. error with heating speed | ± 5°C under 50°C/ h, ± 1°C under 120°C/ h |
| Range of deformation | 0 to 10 mm |
| Vacuum degree | 0 to 90 KPa |
| Accuracy | 1 % FS |
| Resolution | 0.1 KPa |
| Vacuum chamber effective size | 270 × 210 mm |
| Measuring range | 0.01 to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm/ 10 min (MVR), 0.001 to 9.999 g/cm (melt density) |
| Measuring rate | 0.001 S |
| Temperature range | 50 to 400°C |
| Temperature precision | ± 0.5°C |
| Sample (size) length | 38×70 mm |
| Measuring range | (1-500) mN.m (divided into 7 small ranges) |
| Indication error | 0.02 |
| Test speed | (200° ± 20°)/ min |
| Sample (size) length | Diameter ≥30 mm, Thickness ≤ 40 mm |
| System | D/0 lighting geometrical viewing conditions, diffuser diameter (d) 150mm, testing hole diameter 30mm |
| Light source | D65 as illuminating source |
| Zero drift | ≤ 0.1 % |
| Sample (size) length | Diameter ≥30 mm, Thickness ≤ 40 mm |
| Measurement mode | Diffuse reflection factor Rx, Ry, Rz, stimulus value Y10, X10, Z10, chromaticity coordinates x10, y10, z10; lightness L *, chroma a * b *, chroma C * ab, hue angle h * ab, dominant wavelength λd, excitement purity Pe, color difference ΔE * ab, lightness difference ΔL *, chroma difference ΔC * ab, hue difference ΔH * ab, Hunter system L , A, b |
| Stability | ≤ 0.1 within 30 min |
| Accuracy | Chromaticity co-ordinate 0.0001 |
| Resolution | 0.1 % O2 |
| Measuring range | 0 to 100 % O2 |
| Precision | ± 0.4 % O2 |
| Response time | < 10 S |
| The maximum temperature | 300°C |
| Temperature fluctuation | Within ± 0.5°C |
| Temperature uniformity | Within ± 1°C |
| Rotate speed of the turntable | 11 r/min to 12r/min, turntable dimension diameter: 285 mm |
| Vacuum degree | 0 to 90 KPa |
| Accuracy | 1 % FS |
| Resolution | 0.1 KPa |
| Vacuum chamber effective size | 270 × 210 mm |
| Measuring range | 0.001 to 9999 |
| Stability | A (absorbency of light) <0.003 within 3 mins |
| Linearity error | <3.0 % |
| Repeatability error | A (absorbency of light) <0.005 |
| Salinity Measurement range | 0.00 to 19.99 ms/cm |
| Measuring accuracy | EC ± 2% full scale |
| Temperature Measurement range | -5 to 50°C |
| Temperature accuracy | ± 0.5°C |
| Measuring range | 0.001 to 9999 |
| Stability | A (absorbency of light) <0.003 within 3 mins |
| Linearity error | <3.0 % |
| Repeatability error | A (absorbency of light) <0.005 |
| Test angle | 60° |
| Gloss aperture | 2 × 3 mm |
| Measurement range | 0 to 1000 GU |
| Repeatability | 0.2 GU (0 to 100 GU), 0.2 % GU (100 to 1000 GU) |
| Temperature control range | Room temperature to -70 ℃ (room temperature ≤ 25 ℃） |
| Temperature accuracy | ± 0.3 ℃ |
| Impact speed | 0℃ to -30℃ around 2.5 ℃/min </br> -30℃ to -40℃ around 2.5 ℃/min </br> -40℃ to -70℃ around 2.0 ℃/min</br> |
| Max dimension L × W × H | 910 × 510 × 860 mm |
| Mixed capacity | 0.5 to 1 kg, 2 to 3 kg, 5 to 7 kg |
| Temperature range | RT to 300°C |
| Temperature control system | PID control |
| Display | LED display |
| Test arm weight | 2.5 N |
| Additional Loads | 2.5 ± 0.1 N, 5 ± 0.1 N, 10 ± 0.1 N, |
| Idler | 150 mm |
| Abrasion stroke | 40 ± 0.2 M |