TNRR-A10 is a No rotor rheometer where rubber sample is enclosed in mold cavity, maintained at test temperature. The mold cavity comes in two parts, where lower part (swing oscillations) determines strain as the reaction torque of the mold cavity (force). The PID controlled microprocessor technology controls and detects change in temperature. LCD screen display the real vulcanization curve and temperature curve, adjust the test data, store test results.
| Temperature tester | Room temperature to 200°C |
| Temperature display resolution | 0.1°C |
| Temperature control accuracy | ≤ ± 0.3°C |
| Rotor speed | 100 times/ min |
| Die cavity frequency | 1.7 Hz |
| Sway angle | ± 0.5°, ± 1°, ± 3° |
| Air compression | 0.5 MPa to 0.65 MPa |
| Ambient temperature | 0 to 35°C |
| Test result | Printed date, time, temperature, vulcanization curve, temperature curve ML, MH, ts1, ts2, t10, t50, Vc1, Vc2 |
| Display | Windows 7 + software |
| Torque range | 0 to 5 NM, 0 to 10 NM, 0 to 20 NM |
| Torque resolution | 0.001 NM |
| Product dimension | 1310 × 560 × 620 mm |
| Weight | 250 kg |
| Power supply | Single phase, 220 V ± 10%, 50 Hz |
| Temperature range | -60°C to 0°C |
| Temperature accuracy | ± 0.5°C |
| Mixed capacity | 0.5 to 1 kg, 2 to 3 kg, 5 to 7 kg |
| Temperature range | RT to 300°C |
| Temperature control system | PID control |
| Test arm weight | 2.5 N |
| Additional Loads | 2.5 ± 0.1 N, 5 ± 0.1 N, 10 ± 0.1 N, |
| Idler | 150 mm |
| Temperature control range | Room temperature to -70 ℃ (room temperature ≤ 25 ℃） |
| Temperature accuracy | ± 0.3 ℃ |
| Impact speed | 0℃ to -30℃ around 2.5 ℃/min </br> -30℃ to -40℃ around 2.5 ℃/min </br> -40℃ to -70℃ around 2.0 ℃/min</br> |
| Temperature range | RT 50° to 300° |
| Temperature accuracy | ± 1° |
| Measuring range | 0.01 to 25 mm |
| Sample (size) length | 0 to 200 mm adjustable |
| Sample width | 15 mm |
| Measuring range | 0 to 30 N (tissue paper), 0 to 100 N,0 to 300 N, 0 to 500 N, 0 to 1000 N |
| Measuring scope | ( 1 to 9999) s, divided in to (1 to 15) s, (15 to 300) s, (300 to 9999) s, the automatic (no. more than 200 s) |
| Sample (size) length | 90 to 200 mm |
| Sample width | 15 mm, 25 mm, 50mm |
| Measuring range | 0 to 30, 0 to 100 N,0 to 300 N |
| Sample (size) length | 38×70 mm |
| Measuring range | (1-500) mN.m (divided into 7 small ranges) |
| Measurement range | 0.01 to 10 N |
| Slider weight | 200 g |
| Slider size | 63×63 mm |
| Sample (size) length | 180 mm (180, 150, 100, 90, 50 mm adjustable) |
| Sample width | 15 mm |
| Measuring range | 0 to 30, 0 to 100 N,0 to 300 N, 0 to 500 N, 0 to 1000 N |
| Sample size (L*B) | 230×50 mm (can join short samples together) |
| Rub pressure | 20 ± 0.2 N |
| Friction speed | 43 times / min |
| Measuring range | A (1 to 6) J indicating error ± 0.05 J<br/> B (1 to 12) J indicating error ± 0.05 J<br/> C (1 to 24) J indicating error ± 0.05 J<br/> D (1 to 48) J indicating error ± 0.05 J<br/> The indicating errors w.r.t measurement range of 20 to 80 % |
| Measuring range | 0.01 to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm/ 10 min (MVR), 0.001 to 9.999 g/cm (melt density) |
| Measuring rate | 0.001 S |
| Temperature range | 50 to 400°C |
| Measuring range | 0.01to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm3/ 10 min (MVR), 0.001 to 9.999 g/ cm3 (melt density) |
| Measuring rate | 0.001 S |
| Temperature range | 50 to 400°C |
| The maximum temperature | 300°C |
| Temperature fluctuation | Within ± 0.5°C |
| Temperature uniformity | Within ± 1°C |
| Standard roller | 2000 ± 50 g |
| Testing stations | 3 |
| Dimension (L*W*H) tester | 320×210×550 mm (3 stations) |
| Inclined adjustable angle | 0 to 40° |
| Panel width | 120 mm |
| Test area width | 80 mm |
| Standard roller | 2000 ± 50 g |
| Testing stations | 6 |
| Dimension (L*W*H) tester | 650×210×550 mm (6 stations) |
| Impact Speed & Energy (charpy) | 2.9 m/s for 1J, 2J, 4J, 5J & 3.8 m/s for 7.5J, 15J, 25J |
| Impact energy (Izod) | 3.5 m/s for 1J, 2J, 4J, 5J, 7.5J, 15J, 25J |
| Resolution of impact energy | 0.001 J |
| Seal temperature | Room temperature -250°C |
| Control accuracy | ± 0.2°C |
| Dwell time | 0.1 S to 999.9 S |
| Operating temperature | Ambient temperature to 300°C |
| Heating rate | 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min) |
| Maximum temp. error with heating speed | ± 5°C under 50°C/ h, ± 1°C under 120°C/ h |
| Preliminary test force | 98 N |
| Total test force | 588, 980, 1471 N |
| Brinell hardness test | 306, 613, 1839 N |
| Frequency (continually adjustable) | 10 Hz to1280 Hz + 0.01 % |
| Amplitude acceleration ( at 30m/s2 pk ) | 40 Hz to 320 Hz + 0.3 dB + 1 digit |
| Amplitude velocity ( at 25mm / sec pk ) | 40 Hz to 320 Hz + 0.5dB +1 digit |
| Test force | 612.5 N, 980 N, 1225 N |
| Brinell hardness test | 1837.5 N, 2450 N, 4900 N/7350 N, 9800 N, 14700 N/29400 N |
| Hardness measuring area | 8 to 650 HBW (hard metals steel ball) |
| Maximum load | 100 kg ( kg and N can be switched automatically) |
| Resolution | 0.01 g |
| Accuracy | ± 0.5 % |
| Salinity Measurement range | 0.00 to 19.99 ms/cm |
| Measuring accuracy | EC ± 2% full scale |
| Temperature Measurement range | -5 to 50°C |
| Measurement range | 0 to 90 % |
| Resolution | 0.1 or 0.01 |
| Accuracy | ± 5 % n (non-saturation condition) |
| Measuring range | 0.001 to 9999 |
| Stability | A (absorbency of light) <0.003 within 3 mins |
| Linearity error | <3.0 % |
| Maximum load | 100 kg ( kg and N can be switched automatically) |
| Resolution | 0.01 g |
| Accuracy | ± 0.5 % |
| Measuring range | 0.001 to 9999 |
| Stability | A (absorbency of light) <0.003 within 3 mins |
| Linearity error | <3.0 % |
| Measurement range | 0 to 60 % |
| Resolution | 0.1 |
| Accuracy | ± 5 % n (non-saturation condition) |
| Measurement range | 0 to 80 % |
| Resolution | 0.1 |
| Accuracy | ± 2 % n (non-saturation condition) |