Lasting adhesive tester TLAT-A10 comes with test plate having adhesive specimen hanged virtually on the stand & its bottom is attached with standard weight. The lasting adhesive property could be obtained by measuring the displacement of specimen on vertical test plate or the time to failure at such load. Equipped with 3 or 6 stations to perform group tests as well as to conduct individual test at each station. The auto timing & locking functions provides highly accurate test results. The standard test plates & weights ensures the accuracy of the test results data.
| Standard roller | 2000 ± 50 g |
|---|---|
| Testing stations | 3 |
| Dimension (L*W*H) tester | 320×210×550 mm (3 stations) |
| Weight for stations | 10 kg (3 stations) |
| Weight of the plates | 1000 ± 3 g ( with triangle hook) |
| Test plate (L*W*H) | 125×50×1.5 mm |
| Timing range | 0 to 99 h 59 min 59 S |
| Power | AC 220 V, 50 Hz |
Lasting adhesive tester has applications in plastic & packaging industry, stationary making industry.
| Temperature range | 10 to 35°C |
| Maximum falling height | 2000 mm |
| Resolution of displacement | 1 mm |
| Height error | < ± 2 mm |
| Vacuum degree | 0 to 90 KPa |
| Accuracy | 1 % FS |
| Resolution | 0.1 KPa |
| Vacuum chamber effective size | 270 × 210 mm |
| Measuring range | 0.01 to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm/ 10 min (MVR), 0.001 to 9.999 g/cm (melt density) |
| Measuring rate | 0.001 S |
| Temperature range | 50 to 400°C |
| Temperature precision | ± 0.5°C |
| Resolution | 0.1 % O2 |
| Measuring range | 0 to 100 % O2 |
| Precision | ± 0.4 % O2 |
| Response time | < 10 S |
| Inclined adjustable angle | 0 to 40° |
| Panel width | 120 mm |
| Test area width | 80 mm |
| Standard steel balls | 1/32 to 1 inch |
| Impact Speed & Energy (charpy) | 2.9 m/s for 1J, 2J, 4J, 5J & 3.8 m/s for 7.5J, 15J, 25J |
| Impact energy (Izod) | 3.5 m/s for 1J, 2J, 4J, 5J, 7.5J, 15J, 25J |
| Resolution of impact energy | 0.001 J |
| Pendulum up angle | 160° |
| Measuring range | 0.01to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm3/ 10 min (MVR), 0.001 to 9.999 g/ cm3 (melt density) |
| Measuring rate | 0.001 S |
| Temperature range | 50 to 400°C |
| Temperature precision | ± 0.5°C |
| Operating temperature | Ambient temperature to 300°C |
| Heating rate | 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min) |
| Maximum temp. error with heating speed | ± 5°C under 50°C/ h, ± 1°C under 120°C/ h |
| Range of deformation | 0 to 10 mm |
| The maximum temperature | 300°C |
| Temperature fluctuation | Within ± 0.5°C |
| Temperature uniformity | Within ± 1°C |
| Rotate speed of the turntable | 11 r/min to 12r/min, turntable dimension diameter: 285 mm |
| Standard roller | 2000 ± 50 g |
| Testing stations | 6 |
| Dimension (L*W*H) tester | 650×210×550 mm (6 stations) |
| Weight for stations | 15 kg (6 stations) |
| Seal temperature | Room temperature -250°C |
| Control accuracy | ± 0.2°C |
| Dwell time | 0.1 S to 999.9 S |
| Dwell pressure | 0.05 to 0.7 MPa |
| Vacuum degree | 0 to 90 KPa |
| Accuracy | 1 % FS |
| Resolution | 0.1 KPa |
| Vacuum chamber effective size | 270 × 210 mm |
| Resolution | 0.1 % O2 |
| Measuring range | 0 to 100 % O2 |
| Precision | ± 0.4 % O2 |
| Response time | < 10 S |
| The maximum temperature | 300°C |
| Temperature fluctuation | Within ± 0.5°C |
| Temperature uniformity | Within ± 1°C |
| Rotate speed of the turntable | 11 r/min to 12r/min, turntable dimension diameter: 285 mm |
| Salinity Measurement range | 0.00 to 19.99 ms/cm |
| Measuring accuracy | EC ± 2% full scale |
| Temperature Measurement range | -5 to 50°C |
| Temperature accuracy | ± 0.5°C |
| Measuring range | 0.001 to 9999 |
| Stability | A (absorbency of light) <0.003 within 3 mins |
| Linearity error | <3.0 % |
| Repeatability error | A (absorbency of light) <0.005 |
| Measuring range | 0.001 to 9999 |
| Stability | A (absorbency of light) <0.003 within 3 mins |
| Linearity error | <3.0 % |
| Repeatability error | A (absorbency of light) <0.005 |
| Mixed capacity | 0.5 to 1 kg, 2 to 3 kg, 5 to 7 kg |
| Temperature range | RT to 300°C |
| Temperature control system | PID control |
| Display | LED display |
| Temperature control range | Room temperature to -70 ℃ (room temperature ≤ 25 ℃） |
| Temperature accuracy | ± 0.3 ℃ |
| Impact speed | 0℃ to -30℃ around 2.5 ℃/min </br> -30℃ to -40℃ around 2.5 ℃/min </br> -40℃ to -70℃ around 2.0 ℃/min</br> |
| Max dimension L × W × H | 910 × 510 × 860 mm |
| Test arm weight | 2.5 N |
| Additional Loads | 2.5 ± 0.1 N, 5 ± 0.1 N, 10 ± 0.1 N, |
| Idler | 150 mm |
| Abrasion stroke | 40 ± 0.2 M |
| Test angle | 60° |
| Gloss aperture | 2 × 3 mm |
| Measurement range | 0 to 1000 GU |
| Repeatability | 0.2 GU (0 to 100 GU), 0.2 % GU (100 to 1000 GU) |
| Sample (size) length | Diameter ≥30 mm, Thickness ≤ 40 mm |
| Measurement mode | Diffuse reflection factor Rx, Ry, Rz, stimulus value Y10, X10, Z10, chromaticity coordinates x10, y10, z10; lightness L *, chroma a * b *, chroma C * ab, hue angle h * ab, dominant wavelength λd, excitement purity Pe, color difference ΔE * ab, lightness difference ΔL *, chroma difference ΔC * ab, hue difference ΔH * ab, Hunter system L , A, b |
| Stability | ≤ 0.1 within 30 min |
| Accuracy | Chromaticity co-ordinate 0.0001 |
| Sample (size) length | Diameter ≥30 mm, Thickness ≤ 40 mm |
| System | D/0 lighting geometrical viewing conditions, diffuser diameter (d) 150mm, testing hole diameter 30mm |
| Light source | D65 as illuminating source |
| Zero drift | ≤ 0.1 % |
| Sample (size) length | 38×70 mm |
| Measuring range | (1-500) mN.m (divided into 7 small ranges) |
| Indication error | 0.02 |
| Test speed | (200° ± 20°)/ min |